Airgeltech's aerogel slurry provides 0.018 W/m·K thermal insulation with UL94 V0 fireproofing. Ideal for EV batteries, industrial pipes, and building coatings. Request technical docs for viscosity and application guidelines.
AIRG‑S Aerogel Slurry
Dust‑free, water‑based SiO₂ aerogel dispersion for spray‑on or roll‑on thermal‑insulation coatings.
Key metrics
· Thermal conductivity (dry film): 0.018 W m⁻¹ K⁻¹ @ 25 °C (ASTM C177)
· Bulk density (dry): ≈ 60 kg m⁻³
· Contact angle (restored): > 150 °
· Solids content: 25 ± 2 wt %
Why AIRG‑S?
1. Dust‑free handling – eliminates airborne silica during mixing or spraying.
2. One‑step hydrophobic recovery – slurry is stable in water; films become water‑repellent after curing.
3. Ultra‑lightweight – cuts coating weight by 50 % versus acrylic hollow‑glass‑bead systems.
4. Versatile formulation window – compatible with acrylic, silicate and PU water‑borne binders at 5‑15 phr.
Typical applications
Sector | Use case | Benefit |
Architectural coatings | Exterior cool‑roof paints | ↓ 30 % HVAC load, emissivity 0.90 |
Prefabricated panels | Aerogel‑perlite composites | λ ≤ 0.022 W m⁻¹ K⁻¹ at 10 mm |
EV battery packs | 0.5 mm inner‑lid coating | Delays thermal runaway ≥ 10 min (UL 9540A test data) |
Industrial pipes | Spray‑applied wrap | Same R‑value as 5 mm mineral wool in 1 mm dry film |
Processing guide summary
· Storage: 5–30 °C, sealed; shelf‑life 6 months.
· Mixing: slow‑speed paddle, 300 rpm, 5 min; de‑air 10 min.
· Recommended loading: 5–15 phr on resin solids; adjust viscosity with water or rheology modifiers.
Certificates: ISO 9001 • RoHS • UL 94 V‑0
Next step: Request the AIRG‑S Formulation Handbook or a 5 kg pilot batch.
(Note: Parameters can be adjusted per customer requirements; actual performance depends on testing data.)